Anticorrosion coated stainless steel as durable support for C-N-TiO2 photo catalyst layer
(MDPI, 2020)
The development of durable photocatalytic supports resistant in harsh environment has become challenging in advanced oxidation processes (AOPs) focusing on water and wastewater remediation. In this study, stainless steel ...
Effect of calcination time on the physicochemical properties and photocatalytic performance of carbon and nitrogen co-doped TiO2 nanoparticles
(MDPI, 2020)
The application of highly active nano catalysts in advanced oxidation processes (AOPs)
improves the production of non-selective hydroxyl radicals and co-oxidants for complete remediation
of polluted water. This study ...
Corrosion improvement of 304l stainless steel by zrsin and zrsi(N,o) mono-and double-layers prepared by reactive cathodic arc evaporation
(MDPI, 2021)
Zr-based nitrides and oxynitrides were deposited by reactive cathodic arc evaporation in
monolayer and double-layer structures with the aim of increasing the corrosion protection of 304L
stainless steel (SS) in a biomedical ...
Effects of Film Thickness of ALD-Deposited Al2O3, ZrO2 and HfO2 Nano-Layers on the Corrosion Resistance of Ti(N,O)-Coated Stainless Steel
(MDPI, 2023)
The goal of this stydy was to explore the potential of the enhanced corrosion resistance of
Ti(N,O) cathodic arc evaporation-coated 304L stainless steel using oxide nano-layers deposited by
atomic layer deposition (ALD). ...
Effects of film thickness of ALD-deposited Al2O3, ZrO2 and HfO2 nano-layers on the corrosion resistance of Ti(N,O)-coated stainless steel
(MDPI, 2023)
The goal of this stydy was to explore the potential of the enhanced corrosion resistance of Ti(N,O) cathodic arc evaporation-coated 304L stainless steel using oxide nano-layers deposited by atomic layer deposition (ALD). ...
Effects of film thickness of ald-deposited al2o3, zro2 and hfo2 nano-layers on the corrosion resistance of ti(n,o)-coated stainless steel
(MDPI, 2023)
The goal of this stydy was to explore the potential of the enhanced corrosion resistance of
Ti(N,O) cathodic arc evaporation-coated 304L stainless steel using oxide nano-layers deposited by
atomic layer deposition (ALD). ...